簡要描述：This product contains full area coverage MoS2 monolayers on SiO2/Si substrates. Sample size measures 1cm in size and the entire sample surface contains monolayer thick MoS2 sheet.

更新時間：2024-06-03
產(chǎn)品型號：
廠商性質(zhì)：生產(chǎn)廠家
訪問量：1541

產(chǎn)品咨詢聯(lián)系我們

產(chǎn)品分類

二維材料

鈣鈦礦/OLED 異質(zhì)結 MOFS材料其他二維材料二維材料溶液二維材料薄膜二維材料粉末絕緣體黑磷六方氮化硼晶體碲化物晶體硒化物晶體硫化物晶體查看全部產(chǎn)品

詳細介紹

This product contains full area coverage MoS2 monolayers on SiO2/Si substrates. Sample size measures 1cm in size and the entire sample surface contains monolayer thick MoS2 sheet. Synthesized full area coverage monolayer MoS2 is highly luminescent and Raman spectroscopy studies also confirm the monolayer thickness. In comparison to full area coverage MoS2 on sapphire, full area coverage MoS2 on SiO2/Si display higher PL intensity.

Sample Properties.

Sample size	1cm x 1cm square shaped
Substrate type	Thermal oxide (SiO2/Si) substrates
Coverage	Full Coverage Monolayer
Electrical properties	1.85 eV Direct Bandgap Semiconductor
Crystal structure	Hexagonal Phase
Unit cell parameters	a = b = 0.313 nm, c = 1.230 nm, α = β = 90°, γ = 120°
Production method	Atmospheric Pressure Chemical Vapor Deposition (APCVD)
Characterization methods	Raman, photoluminescence, TEM, EDS

Specifications

1) Identification. Full coverage 100% monolayer MoS2 uniformly covered across SiO2/Si substrates.

2) Physical dimensions. One centimeter in size. Larger sizes up to 2-inch wafer-scale available upon requests.

3) Smoothness. Atomically smooth surface with roughness < 0.2 nm.

4) Uniformity. Highly uniform surface morphology. MoS2 monolayers uniformly cover across the SiO2/Si substrates.

5) Purity. 99.9995% purity as determined by nano-SIMS measurements

6) Reliability. Repeatable Raman and photoluminescence response

7) Crystallinity. High crystalline quality, Raman response, and photoluminescence emission comparable to single crystalline monolayer flakes.

8) Substrate. SiO2/Si substrates. But our research and development team can transfer MoS2 monolayers onto variety of substrates including PET and quartz without significant compromisation of material quality.

9) Defect profile. MoS2 monolayers do not contain intentional dopants or defects. However, our technical staff can produce defected MoS2 using α-bombardment technique.

Supporting datasets [for 100% Full area coverage on SiO2/Si]

Transmission electron images (TEM) acquired from CVD grown full area coverage MoS2 monolayers on SiO2/Si confirming highly crystalline nature of monolayers

Energy dispersive X-ray spectroscopy (EDX) characterization on CVD grown full area coverage MoS2 on SiO2/Si confirming Mo:S 1:2 ratios

Room temperature photoluminescence spectroscopy (PL) and Raman spectroscopy (Raman) measurements performed on CVD grown full area coverage MoS2 monolayers on SiO2/Si. Raman spectroscopy measurement confirm monolayer nature of the CVD grown samples and PL spectrum display sharp and bright PL peak located at 1.85 eV in agreement with the literature.

產(chǎn)品咨詢

留言框

產(chǎn)品：
您的單位：
您的姓名：
聯(lián)系電話：
常用郵箱：
省份：
詳細地址：
補充說明：
驗證碼：

請輸入計算結果（填寫阿拉伯數(shù)字），如：三加四=7

上一篇：基于藍寶石襯底的全區(qū)域覆蓋的單層二硫化錸
下一篇：藍寶石襯底的全區(qū)域覆蓋的單層二硫化鉬

二氧化硅襯底的全區(qū)域覆蓋的單層二硫化鉬

留言框

產(chǎn)品：

您的單位：

您的姓名：

聯(lián)系電話：

常用郵箱：

省份：

詳細地址：

補充說明：

驗證碼：